Ingots

Aluminij Industries produces quality foundry alloys as mold cast ingots. Alloys DIN226, ADC12, and A380 are used for die-casting and have high castability, low density, high productivity, low shrinking rate, and relatively high strength. These properties make it useful mostly in the automobile industry.

CHEMICAL COMPOSITION
Alloy Si Fe Cu Mn Mg Cr Ni Zn Ti Sn Pb Each Total Aluminium (min)
DIN226 8-11% 1% 2-3.5% 0.1-0.4% 0.1-0.5% - 0.3% 1.2% 0.15% 0.1% 0.2% - 0.15% Reminder
ADC12 9.6-12% ≤1.3% 1.5-3.5% ≤0.5% ≤0.3% - ≤0.5% ≤1.0% ≤0.30% ≤0.2% ≤0.2% - - Reminder
A380 7.5-9.5% 1.3% 3-4% ≤0.5% ≤0.1% - ≤0.5% ≤3% ≤- ≤0.35% ≤- - 0.5% Reminder
MECHANICAL PROPERTIES
Alloy Elongation % in 50mm Tensile Strength MPa Yield Strength (%0.2%) MPa Impact Strength J Hardness Brinell (HB)
DIN226 3.5 310 150 4 75
ADC12 3.5 310 150 4 75
A380 3.5 310 150 4 75
PHYSICAL PROPERTIES
Alloy Density (g/cm3) Melting Point (Average +/-50)(°C) Thermal Conductivity (W/mK) Coefficient of Thermal Expansion (µm/°K) Electrical Conductivity (%IACS)
DIN226 2.74 549 96 21.1 23
ADC12 2.74 549 96 21.1 23
A380 2.74 549 96 21.1 23

FOUNDRY ALLOYS

Aluminij foundry alloys are a blend of different metallic elements, often created to enhance a specific characteristic of the material, such as strength and durability. An aluminium alloy typically consists of the latter as the main metal in the blend, often combined with other elements, such as silicon, tin, manganese, copper, and magnesium, depending on the specific application of the material produced. These alloys represent a rising trend across many industries, and aluminium as a base material is seen as the material of the future, due to it being light, durable, and recyclable.

With the right combination of elements, great strength of the material can be achieved, and in some cases, aluminum alloys could outperform steel. Aluminij produces a wide range of aluminum alloys, and their quality is ensured by using high-grade raw materials and a meticulous quality control process.

Alloy Si Cu Mg Zn Fe Mn Ti Ni Pb Sn Cd Al
AK5M2 2.0-6.0 2.00 max 0.1-0.85 1.0-1.5 1.00 max 0.2-0.8 0.05-0.20 0.5 max 0.3 max 0.3 max 0.01 max balance
AK5M2 Type-1* 2.0-10.0 2.00 max 0.85 max 1.00 max 1.00 max 0.2-0.8 0.05-0.20 0.50 max 0.3 max 0.3 max 0.01 max balance
AK5M2 Type-2* 2.0-10.0 2.00 max 0.50 max 1.00 max 1.00 max 0.2-0.8 0.05-0.20 0.50 max 0.3 max 0.3 max 0.01 max balance
AK5M2 Type-3* 2.0-10.0 2.00 max 0.3 max 1.00 max 1.00 max 0.2-0.8 0.05-0.20 0.50 max 0.3 max 0.3 max 0.01 max balance
AK5M2 Type-4* 2.0-10.0 2.00 max 0.1 max 1.00 max 1.00 max 0.2-0.8 0.05-0.20 0.50 max 0.3 max 0.3 max 0.01 max balance
AK5M2 Type-5* 2.0-10.0 2.00 max 0.1-0.85 1.00 max 1.00 max 0.2-0.8 0.05-0.20 0.50 max 0.3 max 0.3 max 0.01 max balance